| Flame-retarding component |
| PC/TBA oligomer/(Br=51.1%)/ PTFE=100/5.0/0.5 (part) |
| HIPS/epoxy bromide (Br=50%-52%)/antimony trioxide/PTFE=00/20.0/3.5/0.1 (part) |
| ABS/epoxy bromide (Br=50%-52%)/antimony trioxide/PTFE=100/22.5/7.0/0.39 (part) |
| ABS/epoxy bromide (Br=50%-52%)/antimony trioxide/CPE=100/22.5/7.0/6.5 (part) |
| 2.Good Outer Appearance |
| Because fluororesin spreads well over plastics, molded products come out better looking than conventional PTFE products. They are particularly effective with housings and parts for office equipment and home appliances where outer appearance is important. |
| Molded part in polycarbonate |
 |
|
 |
| With 5% MPA addition |
|
With 5% PTFE addition |
| 3.Good Powder Flowability |
| Fluororesin improves productivity is injection molding |
| Adhesion to mixing vanes after stirring |
 |
|
 |
|
 |
| FA-500 |
|
Conventional PTFE
(F-104) |
|
Conventional PTFE
(F-201L) |
| ¦Other applications |
| POLYFLON MPA powder has good dispersion properties and can also form fibers.These properties can be used in a variety of possible ways. For example,by adding POLYFLON MPA to other plastics, the viscosity of a resin mixture can be increased in the same way as when preventing dripping, so that it can also be used as a viscosity controlling agent. |
|